TCS TWIST 9A2

Barre

TCS TWIST 9A2 is the innovative stainless steel helical bar A2 class used for anchorages, connections and dry seams. The helix shape and strongly hardened steel give the bar a high strength and hardness, thus allowing a mechanical connection.

Product features

The helical bars TCS TWIST 9A2 thanks to the special shape and the strongly hardened stainless steel allow for a totally dry connection without the use of resins or mortars for installation. For the installation in the substrates to be consolidated and/or connect, a pilot perforation must be made for the entire insertion depth.

The bar, during insertion, generates an incision similar to a thread with a constant pitch which allows the interlock of the same to the substrate. The seal of the bar to the substrate is easily verifiable by a pull test with the instrument TCS 3T Tie Twist Tester and based on the type and consistency of the substrate, of the pilot perforation size and the depth of insertion.

ENVIRONMENT FRIENDLY
RESTORATION
RESISTANT
VERSATILE
RECYCLABLE
QUICK
LIGHT
REVERSIBLE
EASY

Main features

  • PRODUCT TYPE: Helical connector for dry insertion
  • TENSILE STRENGTH: > 1110 MPa
  • TENSILE STRENGTH AT BREAK: > 16,7 kN
  • SHEAR STRENGTH AT BREAK: > 16 kN
  • ELASTIC MODULUS: 196 GPa
  • DEFORMATION AT BREAK: 0,56%
  • EQUAL MASS SECTION: > 14,9 mm2
  • DENSITY: 7850 kg/m3
  • PACKAGE: on request per unit
  • STORAGE: In a dry place
  • LENGTH: 200, 400, 600, 1000 mm (other lengths on request) or 10 m roll
  • APPLICATION TEMPERATURE : from +5°C to +32° C

Contact us if you would like to know more about this product?

Fill in the form below and you will be contacted as soon as possible by our expert who will recommend the best solution to your problems

Subscribe to our newsletter

  I declare that I have read and acknowledged the Information drawn up according to Legislative Decree 196/2003 'Code Concerning the Protection of Personal Data' and I give my consent to utilise my personal data in order to make use of the 'Newsletter' service with the methods described in the above-mentioned Information